|Name, Symbol, Number||tantalum, Ta, 73|
|Chemical series||transition metals|
|Group, Period, Block||5, 6, d|
|Atomic mass||180.94788(2) g/mol|
|Electron configuration||[Xe] 4f14 5d3 6s2|
|Electrons per shell||2, 8, 18, 32, 11, 2|
|Density (near r.t.)||16.69 g/cm³|
|Liquid density at m.p.||15 g/cm³|
|Melting point||3290 K
(3017 °C, 5463 °F)
|Boiling point||5731 K
(5458 °C, 9856 °F)
|Heat of fusion||36.57 kJ/mol|
|Heat of vaporization||732.8 kJ/mol|
|Heat capacity||(25 °C) 25.36 J/(mol·K)|
|Crystal structure||cubic body centered|
|Oxidation states||5 (mildly acidic oxide)|
|Electronegativity||1.5 (Pauling scale)|
|Ionization energies||1st: 761 kJ/mol|
|2nd: 1500 kJ/mol|
|Atomic radius||145 pm|
|Atomic radius (calc.)||200 pm|
|Covalent radius||138 pm|
|Magnetic ordering||no data|
|Electrical resistivity||(20 °C) 131 nΩ·m|
|Thermal conductivity||(300 K) 57.5 W/(m·K)|
|Thermal expansion||(25 °C) 6.3 µm/(m·K)|
|Speed of sound (thin rod)||(20 °C) 3400 m/s|
|Speed of sound (thin rod)||(r.t.) 186 m/s|
|Shear modulus||69 GPa|
|Bulk modulus||200 GPa|
|Vickers hardness||873 MPa|
|Brinell hardness||800 MPa|
|CAS registry number||7440-25-7|
Capacitors made with tantalum and its oxide are widely used in portable telephones, pagers, personal computers, and automotive electronics. Tantalum is also used for making carbide tools for metalworking, and for the production of superalloys for jet engine components, chemical process equipment, nuclear reactors, and missile parts. Given its inertness, tantalum is often used in surgical instruments and implants. Tantalum pentoxide is used to make special glass for camera lenses. Tantalum carbide is useful for making extremely hard composites with metals and graphite, and these composites are then used in tool bits.
Tantalum occurs principally in the minerals tantalite [(Fe, Mn) Ta2O6] and euxenite [(Y,Ca,Ce,U,Th)(Nb,Ta,Ti)2O6]. Tantalite is usually found mixed with columbite in an ore called coltan. Other minerals containing tantalum include samarskite and fergusonite.
Tantalum ores are mined in Ethiopia, Australia, Brazil, Egypt, Canada, the Democratic Republic of the Congo, Mozambique, Nigeria, Portugal, Malaysia, and Thailand. The exploitation of resources in the conflict regions of the Congo has raised ethical questions about human rights and endangered wildlife.
Several complicated steps are involved in the separation of tantalum from niobium. Commercially viable production of this element can follow one of several different methods, such as: (a) electrolysis of molten potassium fluorotantalate; (b) reduction of potassium fluorotantalate with sodium; or (c) reacting tantalum carbide with tantalum oxide. Tantalum is also a byproduct from tin smelting.
Tantalum was discovered in Sweden in 1802 by Anders Ekeberg and isolated in 1820 by Jöns Berzelius. Many contemporary chemists believed niobium and tantalum were the same element, until researchers showed (in 1844 and 1866) that niobic and tantalic acids are different compounds. Early investigators were able to isolate just the impure metal, and the first relatively pure, ductile metal was produced by Werner von Bolton in 1903. Wires made with tantalum metal were used for light bulbs until it was replaced by tungsten.
The name tantalum is derived from the Greek mythological character Tantalos, father of Niobe. Tantalus was punished after death by being condemned to stand knee-deep in water with perfect fruit growing above his head, both of which eternally "tantalized" him. If he bent to drink the water, it drained below the level he could reach, and if he reached for the fruit, the branches moved out of his grasp. This was considered similar to tantalum's general non-reactivity—it is unaffected by reagents and is therefore difficult to refine.
Tantalum is a transition metal that lies in period six of the periodic table, between hafnium and tungsten. In addition, it is located in group five (former group 5B), just below niobium, and its chemical properties are similar to those of niobium.
This element is dark, dense, ductile, very hard, and easily fabricated. It is highly conductive of heat and electricity. It is renowned for its resistance to corrosion by acids. At temperatures below 150 °C, it is almost completely immune to attack by the normally aggressive aqua regia. It can be dissolved with hydrofluoric acid or acidic solutions containing the fluoride ion and sulfur trioxide, as well as with a solution of potassium hydroxide. Tantalum's melting point of 3,017 °C (boiling point 5,458 °C) is exceeded only by the melting points of tungsten and rhenium.
Natural tantalum consists of two isotopes: Ta-181 is a stable isotope, and Ta-180m has a half life of over 1015 years (see scientific notation). In addition, numerous radioactive isotopes (atomic mass numbers ranging from 155 to 190) have been produced artificially, with very short half-lives.
The major use for tantalum, as the metal powder, is in the production of electronic components, mainly capacitors and some high-end, audio-grade resistors. Tantalum electrolytic capacitors exploit the tendency of tantalum to form a protective oxide surface layer, using tantalum foil as one plate of the capacitor, the oxide as the dielectric (electrical insulator between plates), and an electrolytic solution as the other plate. Because the dielectric layer can be very thin (thinner than the similar layer in, for instance, an aluminum electrolytic capacitor), high capacitance can be achieved in a small volume. Given the size and weight advantages, tantalum capacitors are attractive for portable telephones, pagers, personal computers, and automotive electronics.
Tantalum is also used to produce a variety of strong, ductile alloys that have high melting points. Alloyed with other metals, it is also used in making carbide tools for metalworking equipment and in the production of superalloys for jet engine components, chemical process equipment, nuclear reactors, and missile parts. Tantalum wires and filaments are used for heating and evaporating metals such as aluminum.
Given that tantalum resists attack by body fluids and is nonirritating, it is widely used in making surgical instruments and implants. The oxide is used to make special glass (with high refractive index) for camera lenses. The metal is also used to make parts for vacuum furnaces.
Compounds containing tantalum are rarely encountered, and the metal does not normally cause problems in the laboratory. Nonetheless, it should be handled with care, taking the usual laboratory precautions. There is some evidence that tantalum compounds can cause tumors, and its metal dust is a fire and explosion hazard.
All links retrieved November 16, 2015.
New World Encyclopedia writers and editors rewrote and completed the Wikipedia article in accordance with New World Encyclopedia standards. This article abides by terms of the Creative Commons CC-by-sa 3.0 License (CC-by-sa), which may be used and disseminated with proper attribution. Credit is due under the terms of this license that can reference both the New World Encyclopedia contributors and the selfless volunteer contributors of the Wikimedia Foundation. To cite this article click here for a list of acceptable citing formats.The history of earlier contributions by wikipedians is accessible to researchers here: